Interline® 850 high solid Epoxy Phenolic
can provide corrosion protection for the internals of steel storage tanks and pipes containing a range of products, including
crude oil, unleaded gasoline blends, MTBE,
jet fuels, caustic solutions, potable water and a selected range of aromatic and
aliphatic solvents.
Surface Preparation:
All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be
assessed and treated in accordance with ISO 8504:2000.
Where necessary, remove weld spatter, and smooth weld seams and sharp edges.
Oil or grease should be removed in accordance with SSPC-SP1 solvent cleaning.
Abrasive Blast Cleaning
This product must only be applied to surfaces prepared by abrasive blast cleaning to a minimum of SSPC-SP10 or Sa2½
(ISO 8501-1:2007).
A sharp, angular surface profile of 2-3 mils (50-75 microns) is recommended.
Interline 850 must be applied before oxidation of the steel occurs. If oxidation does occur the entire oxidized area should be
reblasted to the standard specified above.
Surface defects revealed by the blast cleaning process, should be ground, filled, or treated in the appropriate manner.
Where local VOC regulations allow, surfaces may be primed with Interline 850 (thinned 10-15% GTA415) to 1.5 mils (40
microns) dry film thickness before oxidation occurs. Alternatively, the blast standard can be maintained by use of
dehumidification.
Areas of breakdown, damage, weld seams etc., should be prepared to the specified standard (e.g. SSPC SP10 or Sa2½
(ISO 8501-1:2007) or power tool cleaned to SSPC SP11 or Pt3 (JSRA SPSS:1984)).
Appliation:
Mix Ratio 4 part(s) : 1 part(s) by volume
GP3834 Two Components Sprayer:Tip Range 21-27 thou (0.53-0.68 mm)
Total output fluid pressure at spray tip not less than 2503 psi
(176 kg/cm²)
A plural component spray equipment, chemically resistant, high solids, high build epoxy phenolic tank and pipe lining.
Interline 984 (Heavy duty epoxy phenolic)
is intended as a lining for the protection of ferrous and non-ferrous substrates (including concrete).
It may be used as a single or multi coat scheme, or as either a spray applied fibre reinforced Matcote system or
a hand-lay glass reinforced system.
Interline 984 has been formulated to focus on Oil and Gas downstream lining opportunities with extended recoat
interval designed to assist with the contract schedules associated with lining bulk storage tanks.
Interline 984 is compliant with EI1530 (Joint Industry Group standard). This is the quality assurance requirement
for the manufacture, storage and distribution of aviation fuels to airports.
Interline 984 is resistant to crude oil at temperatures up to 90°C (194°F).
Application:
The detailed Interline 984 Application Guidelines should be consulted prior to use.
Material is supplied in two containers as a unit. Always mix a complete unit in the
proportions supplied. Once the unit has been mixed it must be used within the
working pot life specified.
(1) Agitate Base (Part A) with a power agitator.
(2) Agitate Curing Agent (Part B) with a power agitator.
(3) Combine entire contents of Curing Agent (Part B) with Base
(Part A) and mix thoroughly with power agitator.
Mix Ratio 2 part(s) : 1 part(s) by volume
GP3845 Two Components Sprayer:Tip Range 21-27 thou (0.53-0.68 mm)
Total output fluid pressure at spray tip not less than 211
kg/cm² (3000 p.s.i.)
A two component spraying equipment, solvent free chemically resistant heavy duty epoxy phenolic tank lining.